A283/Q195 Cold Rolled Steel Coil
A283 steel coil exhibits excellent work hardening properties during cold forming for its high strength and plasticity. After repeated cold working deformation, the coil can still show similar strength and hardness, with even better ductility and toughness. In addition, due to its good welding performance, the coil can be easily welded into parts of various shapes and sizes, and the welding quality is stable and reliable. A283 steel coils are widely used in the manufacturing of various mechanical parts, such as bolts, nuts, pins and other standard parts as well as various non-standard mechanical parts. In addition, they are also used in the manufacture of building structural materials.
Product Description
|
Product Name |
A283/Q195 Cold Rolled Steel Coil |
|
Production Process |
Hot Rolling, Cold Rolling |
|
Material Standards |
AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, etc. |
|
Width |
45mm-2200mm |
|
Length |
Custom Size |
|
Thickness |
Hot Rolling: 2.75mm-100mm |
|
Delivery Conditions |
Rolling, Annealing, Quenching, Tempered or Standard |
|
Surface Process |
Ordinary, Wire Drawing, Laminated Film |
Chemical Composition
|
A283 |
Cmax. |
Mnmax. |
Pmax. |
Smax. |
Si (Greater1 inch, less than 1/2 inch) |
Si (Greater 1/2 inch) |
Cumin. |
|
Grade A |
0.14 |
0.90 |
0.035 |
0.04 |
0.40 |
0.15-0.40 |
0.20 |
|
Grade B |
0.17 |
0.90 |
0.035 |
0.04 |
0.40 |
0.15-0.40 |
0.20 |
|
Grade C |
0.24 |
0.90 |
0.035 |
0.04 |
0.40 |
0.15-0.40 |
0.20 |
|
Grade D |
0.27 |
0.90 |
0.035 |
0.04 |
0.40 |
0.15-0.40 |
0.20 |
Mechanical Properties
|
A283 |
Tensile Strength |
Yield Strength min. |
Elongation Rate 8 inches |
Elongation Rate 2 inches |
||
|
Grade A |
45000-60000 psi |
310-415 MPa |
24000 psi |
165 MPa |
27 % min. |
30 % min. |
|
Grade B |
50000-65000 psi |
345-450 MPa |
27000 psi |
185 MPa |
25 % min. |
28 % min. |
|
Grade C |
55000-75000 psi |
380-515 MPa |
30000 psi |
205 MPa |
22 % min. |
25 % min. |
|
Grade D |
60000-80000 psi |
415-550 MPa |
33000 psi |
230 MPa |
20 % min. |
23 % min. |
Physical Performance
|
Physical Performance |
Metric |
Imperial |
|
Density |
7.80 g/cc |
0.282 lb/in³ |
Scope of Application
ASTM A283 steel plate is a kind of low carbon steel with high strength and
good formability. It is easy to process and manufacture, and can be safely
welded by various welding methods. ASTM A283 steel plate is a structural carbon
steel plate used for low or medium tensile strength applications. ASTM A283
steel plate is used in the manufacture of riveted, bolted and welded structures
for storage tanks and cryogenic control vessels, bridges and buildings,
including prefabricated buildings, warehouses and industrial commercial
structures.
Related products
-
Quick View
316L Stainless Steel Plate
Contact Us316L stainless steel has a lower proportion of carbon in its composition. To qualify as 316L stainless steel, the amount of carbon cannot exceed 0.03%.
-
Quick View
309/309S Stainless Steel Pipe
Contact Us309 stainless steel is a stainless steel type with incredible corrosion resistance and high temperature performance. It is widely used in fields such as aviation, chemical industry, and petroleum.
-
Quick View
1070 Aluminum Plate
Contact Us1070 belongs to the pure aluminum series alloys. The aluminum content is greater than 99.7%, and the content of other impurity elements is low.
-
Quick View
304L Stainless Steel Coil
Contact Us304L stainless steel is remarkably similar to 304 stainless steel in their chemical composition with one key difference.
Reviews
There are no reviews yet.