BG6SF11C
Product Name: PA6-GF30Product grade: Injection molding gradeProduct features: 30% glass fiber reinforced nylon 6, with extremely high fluidity, suitable for products with high smoothness requirements.
BG6SF11C-Typical molding process
|
Dry |
Drum wind oven： 100～120℃，4～6h； Cycling warm air： 100～120℃，4～6h； Vacuum drying oven： 100～120℃，3～4h； |
|
Processing temperrature |
Feed section：225～235℃ Compressing section：240～260℃ Metering secion：240～275℃ |
|
Injection pressure |
70～130MPa |
|
Packing pressure |
40～90 MPa |
|
Mold temperature |
70～100℃ |
|
Back pressure |
8～15MPa |
BG6SF11C
|
Test Item |
Test Standard |
Test Condition |
Unit |
Value |
|
Others |
||||
|
Product Identification |
ISO1043 |
—— |
—— |
PA6-GF30 |
|
Filler Content |
ISO3451-1 |
—— |
% |
30 |
|
Density |
ISO1183 |
23℃ |
g/cm³ |
1.37 |
|
Molding shrinkage(parallel/ normal) |
ISO 294-4 |
—— |
% |
0.4/0.6 |
|
Viscosity number |
ISO307 |
96%H2SO4,0.5g/dl |
ml/g |
88 |
|
Mechanical |
||||
|
Flexural Strength |
ISO178 |
23℃，2mm/min |
MPa |
235 |
|
Flexural Modulus |
ISO178 |
23℃，2mm/min |
MPa |
8200 |
|
Tensile Strength |
ISO527 |
Type I spline,50mm/min |
MPa |
165 |
|
Tensile Module |
ISO527 |
Type I spline,1mm/min |
MPa |
/ |
|
Tensile Strain at Break |
ISO527 |
Type I spline,50mm/min |
% |
3 |
|
Charpy Notched Impact Strength |
ISO179/1eA |
23℃ |
kJ/m2 |
15 |
|
Charpy Unnotched Impact Strength |
ISO179/1eU |
23℃ |
kJ/m2 |
78 |
|
Thermal |
||||
|
Melting Temperature |
ISO11357 |
—— |
℃ |
220 |
|
Heat Distortion Temperature |
ISO75-2 |
0.45MPa |
℃ |
215 |
|
1.8MPa |
℃ |
200 |
||
|
Electrical |
||||
|
CTI |
IEC60112 |
A |
V |
/ |
|
Volume Resistivity |
IEC60093 |
—— |
Ω•cm |
1013 |
|
Surface resistivity |
IEC60093 |
—— |
Ω |
1012 |
|
Flammability |
||||
|
Flammability |
UL-94 |
1.6mm |
Class |
HB |
|
GWIT |
IEC60695 |
—— |
℃ |
/ |
|
GWFIT |
IEC60695 |
—— |
℃ |
/ |
All is typical data, only for reference, not the permit of quality assurance.
Related products
-
Quick View
(6-Oxo-3-phenylpyridazin-1(6H)-yl)acetic acid
Contact UsCAS: 91973-93-2 Product Name: (6-Oxo-3-phenylpyridazin-1(6H)-yl)acetic acid
-
Quick View
HZR818 Rutile TiO2 for Plastics & Masterbatch
Contact UsThis rutile titanium dioxide, produced via the sulfate process, is engineered to meet the demanding requirements of the plastics and masterbatch industries.
-
Quick View
Cras viverra rhoncus metu
$77.00Add to cartAenean ut commodo justo. Fusce accumsan erat ut purus mollis, quis fermentum magna luctus. Morbi pulvinar augue lorem, quis molestie ipsum dictum non. Donec malesuada fermentum ex non hendrerit. Sed tempor viverra arcu a ultrices. Suspendisse non malesuada massa. Praesent imperdiet rhoncus nunc, vel fringilla enim lacinia quis
-
Quick View
Silk Amino Acids Solution
Contact UsSilk Amino Acids Solution, mixed amino acid obtained after hydrolysis of silk pigment protein.
Reviews
There are no reviews yet.