BG6UV11
Product Name: BG6UV11Product grade: Injection molding gradeProduct features: 30% glass fiber reinforced nylon 6, UV resistant.
BG6UV11-Typical mollding process
|
Dry |
Drum wind oven: 100～120℃, 4～6h； Cycling warm air: 100～120℃,4～6h； Vacuum drying oven： 100～120℃,3～4h； |
|
Processing temperrature |
Feed section：225～240℃ Compressing section：250～280℃ Metering secion：250～280℃ |
|
Injection pressure |
70～130MPa |
|
Packing pressure |
40～90 Mpa |
|
Mold temperature |
70～100℃ |
|
Back pressure |
5～10Mpa |
BG6UV11
|
Test Item |
Test Standard |
Test Condition |
Unite |
Value |
|
Others |
||||
|
Ash Content |
ISO3451-1 |
620℃ |
% |
30 |
|
Melt Index |
ISO1133 |
250℃，2.16kg |
g/10min |
12 |
|
Density |
ISO1183 |
23℃ |
g/cm³ |
1.30 |
|
Mechanical |
||||
|
Flexural Strength |
ISO178 |
23℃，2mm/min |
MPa |
230 |
|
Flexural Modulus |
ISO178 |
23℃，2mm/min |
MPa |
8500 |
|
Tensile Strength |
ISO527 |
Type I spline,50mm/min |
MPa |
170 |
|
Elongation at Break |
ISO527 |
Type I spline,50mm/min |
% |
5 |
|
Charpy Notched Impact Strength |
ISO179/1eA |
23℃ |
kJ/m2 |
11 |
|
Charpy Unnotched Impact Strength |
ISO179/1eU |
23℃ |
kJ/m2 |
75 |
|
Thermal |
||||
|
Temperature of Deflection Under Load |
ISO75-2 |
0.45MPa |
℃ |
215 |
|
1.8MPa |
℃ |
205 |
||
|
Flammability |
||||
|
Flammability |
UL-94 |
1.6mm |
—— |
HB |
All is typical data, only for reference, not the permit of quality assurance.
Related products
-
Quick View
BG6SF11C
Contact UsProduct Name: PA6-GF30Product grade: Injection molding gradeProduct features: 30% glass fiber reinforced nylon 6, with extremely high fluidity, suitable for products with high smoothness requirements.
-
Quick View
Silk Amino Acids Solution
Contact UsSilk Amino Acids Solution, mixed amino acid obtained after hydrolysis of silk pigment protein.
-
Quick View
Hydroxypropyl Methacrylate (HPMA)
Contact UsAdhesives, rubber compounds & Concrete superplasticizers
-
Quick View
Cras viverra rhoncus metu
$77.00Add to cartAenean ut commodo justo. Fusce accumsan erat ut purus mollis, quis fermentum magna luctus. Morbi pulvinar augue lorem, quis molestie ipsum dictum non. Donec malesuada fermentum ex non hendrerit. Sed tempor viverra arcu a ultrices. Suspendisse non malesuada massa. Praesent imperdiet rhoncus nunc, vel fringilla enim lacinia quis
Reviews
There are no reviews yet.